Bambu Lab PAHT-CF Carbon Fibre Nylon 0.5kg
Filament On Spool
Government and Education
3DPrintergear has been supplying government organisations with 3D printers, services and support since 2012. As an approved government customer you will automatically be entitled to 30-day terms with an official purchase order.
Want to become a reseller?
3DPrintergear offers special pricing to genuine resellers. Once your application is approved, your new buying prices will be shown on our website after you login. To apply for a resellers account please contact us at firstname.lastname@example.org
$10 Flat Rate Shipping - $10.00
Your order will be shipped by the most economical option, with online tracking. Delivery is usually 2-7 business days.
TNT/DHL - Next Day Express Domestic - $10.00
1 day delivery! Please note Business address only. Residential addresses will incur a fee.
Free pick-up from store - FREE
Free pick-up from '781 High St, Reservoir VIC 3073', between 9am and 5pm
- Express Dispatch
- Australian Owned & Operated
- Money Back Guarantee
- Quality Assured Products
Bambu Lab PAHT-CF Carbon Fibre Nylon
Bambu PAHT-CF is a unique composite material that combines PA12 (Nylon 12) and carbon fiber. This composite inherits the low water absorption property of PA12 and the exceptional performance of carbon fiber, resulting in a filament with outstanding mechanical and thermal properties. Even when exposed to moisture, Bambu PAHT-CF maintains its high performance levels.
With higher Z adhesion layers and enhanced flexibility, Bambu PAHT-CF is an excellent choice for creating engineering parts, including functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts. Its superior properties make it ideal for applications where strength, durability, and resistance to moisture are essential. Whether you are in the field of engineering, manufacturing, or product development, Bambu PAHT-CF offers the reliability and performance needed for demanding projects.
Low Water Absorption
Bambu PAHT-CF stands out with its exceptional water resistance, boasting a water absorption rate that is 50% lower than regular PA-CF (Nylon-Carbon Fiber) materials. This lower water absorption rate is a key advantage, as it enables Bambu PAHT-CF to maintain excellent mechanical properties and dimensional stability, even when subjected to high humidity or moisture-rich environments.
The reduced water absorption of Bambu PAHT-CF helps prevent the material from absorbing excessive moisture, which can lead to dimensional changes, warping, and degradation in other materials. By retaining its mechanical properties and dimensional stability, Bambu PAHT-CF ensures reliable and consistent performance throughout its lifespan, even in challenging conditions.
Mechanical Properties Comparison
|Saturated Water Absorption Rate% (25 °C, 55% RH )||1.89||0.88|
|Bending Strength - XY/MPa (Dry)||141||140|
|Bending Strength - XY/MPa (Wet)||76||115|
|Bending Strength - Z/MPa (Dry)||47||70|
|Bending Strength - Z/MPa (Wet)||34||58|
|Bending Modulus - XY/MPa (Dry)||4480||4120|
|Bending Modulus - XY/MPa (Wet)||2210||3640|
|Bending Modulus - Z/MPa (Dry)||1470||1700|
|Bending Modulus - Z/MPa (Wet)||770||1480|
|Decline rate of mechanical properties after absorbing water/%||40%-45%||12%-18%|
Bambu PAHT-CF exhibits superior adhesion in Z layers compared to regular PA-CF (Nylon-Carbon Fiber) materials. This enhanced adhesion contributes to its exceptional ability to withstand high levels of impact or stress without breaking or deforming.
The improved Z layer adhesion of Bambu PAHT-CF ensures strong interlayer bonding, resulting in a more robust and durable printed part. This means that the material can effectively distribute and absorb impact forces, making it highly resistant to fractures or deformations even under demanding conditions.
|Normal PA-CF||PAHT-CF||Improved %|
|Bending Strength - Z/MPa||47||70||49%|
|Bending Modulus - Z/MPa||1470||1700||16%|
|Impact Strength - Z/(kJ/m²)||5.7||13.3||133%|
Bambu PAHT-CF has been specifically developed to cater to the requirements of a wide range of industrial and engineering applications that demand exceptional strength and durability. With its unique composition of PA12 (Nylon 12) and carbon fiber, Bambu PAHT-CF offers outstanding mechanical properties and performance characteristics, making it an ideal choice for demanding applications.
The material's high strength and durability ensure that printed parts can withstand heavy loads, impacts, and repetitive stresses without compromising their structural integrity.
|Build Plate||High-Temperature Plate Engineering Plate||Cool Plate|
|Hotend||Hotend with Hardened Steel Nozzle (0.6 mm, 0.4 mm, 0.8 mm)*||Hotend with Stainless Steel Nozzle (all size)
Hotend with Hardened Steel Nozzle (0.2 mm)
|Glue||Glue Stick||Liquid Glue|
Resistance to High Temperatures
Bambu PAHT-CF exhibits an impressive heat deflection temperature of up to 194℃ (0.45MPa), making it a highly suitable material for applications where printed parts may be subjected to elevated temperatures. This high heat resistance ensures that the parts retain their structural integrity and strength even when exposed to demanding thermal conditions.
With its ability to withstand elevated temperatures without deforming or losing its mechanical properties, Bambu PAHT-CF opens up possibilities for a wide range of applications. It can be used in environments where high-temperature stability is essential, such as under-the-hood automotive components, electrical enclosures, industrial equipment, and other heat-intensive applications.
|Price/kg||$129.99 AUD||$144.99 AUD|
|Composition||PET, carbon fiber||PA 12 and other long-chain PA, carbon fiber|
|Hotend Compatibility||Hardened Steel 0.6 (recommended), 0.4, 0.8 mm|
|Build Plate Compatibility||Engineering Plate, High Temperature Plate, Textured PEI Plate|
|Glue||Glue Stick / Liquid Glue||Glue Stick|
|Print Speed||< 100 mm/s||< 100 mm/s|
|Toughness (Impact Strength - XY)||36.0 kJ/m²||57.5 kJ/m²|
|Strength (Bending Strength - XY)||149 MPa||140 MPa|
|Stiffness (Bending Modulus - XY)||5080 MPa||4120 MPa|
|Layer Adhesion (Impact Strength - Z)||4.5 kJ/m²||13.3 kJ/m²|
|Saturated Water Absorption Rate / % (25 °C，55% RH)||0.37||0.89|
|Heat Resistant（HDT, 0.45 MPa）||205 °C||194 °C|
Smart Printing with RFID
With Bambu PAHT-CF, all the essential printing parameters are conveniently embedded in an RFID chip. This RFID chip can be read by our AMS (Automatic Material System), eliminating the need for manual configuration and tedious setup steps.
Simply load the filament onto the printer, and the AMS will automatically detect the material and retrieve the corresponding printing parameters from the RFID chip. This streamlined process saves you time and effort, allowing you to start printing right away without the hassle of adjusting settings.
Say goodbye to manual parameter input and enjoy a more seamless and efficient printing experience with Bambu PAHT-CF and our integrated AMS technology.
Recommended Printing Settings
|Drying Settings before Printing||80 °C, 8 - 12 h|
|Printing and Keeping Container's Humidity||< 20% RH (Sealed, with Desiccant)|
|Nozzle Temperature||260 - 290 °C|
|Bed Temperature (with PVP Glue)||80 - 100 °C|
|Printing Speed||< 100 mm/s|
|Vicat Softening Temperature||220 °C|
|Heat Deflection Temperature||194 °C|
|Melting Temperature||225 °C|
|Melt Index||14.4 ± 2.0 g/10 min|
|Tensile Strength||88 ± 7 MPa|
|Breaking Elongation Rate||10.4 ± 0.7 %|
|Bending Modulus||4120 ± 290 MPa|
|Bending Strength||140 ± 8 MPa|
|Impact Strength||57.5 ± 3.4 kJ/m²|