Zortrax Z-Resin Basic White  0.5Lt

Zortrax Resin BASIC is an epoxy-based resin offering sharp edges, high detail, and short curing times. It’s durable and easy to print. It’s available in grey, white, and pigment free. Zortrax Resin BASIC contains no volatile organic compounds, so it is safe to print with when used in accordance with our safety instructions.

The already cured resin is easy to paint. This resin has very low shrinkage.

Its shore hardness is 82.2 D for the pigment-free version and as high as 88 D for ivory and grey versions.

Due to its composition, Zortrax Resin BASIC offers smooth surfaces. It can be cured with UV light with 405 nm wavelength.

 

White/Ivory; Grey		Pigment-free
Mechanical Properties	Metric	Imperial	Metric	Imperial
Tensile strength	36  -52 MPa	5220 - 7540 psi	35.7 MPa	5180 psi
Tensile Modulus	1.779 - 2.385 GPa	258 - 346 ksi	-	-
Elongation at Break	11 - 20%	11 - 20%	3%	3%
Flexural Strength	59 - 70 MPa	8560 - 10200 psi	-	-
Flexural Modulus	1.882 - 2.385 GPa	273 - 346 ksi	1.56 GPa	226 ksi
Izod Impact, Notched	44 - 49 J/m	0.824 - 0.918 ft-lb/in	-	-
Other Properties	Metric	Imperial	Metric	Imperial
Viscosity	150 - 200 mPa*s	0.00313 - 0.00418 lbf-s/ft2	33 - 57 mPa*s	0.000689 - 0.00119 lbf-s/ft2
Density	1.05 - 1.13 g	0.00232 - 0.00249 lb	-	-
Shrinkage	3.72 - 4.24%	3.72 - 4.24%	2% +/- 1%	2% +/- 1%
Shore Hardness (D)	88	88	82.2	82.2
Glass Transition Temperature	100° C	212° F	-	-
Hot Deformation Temperature	80° C	176° F	-	-

 

White/Ivory; Grey		Pigment-free
Mechanical Properties	Metric	Imperial	Metric	Imperial
Tensile strength	36  -52 MPa	5220 - 7540 psi	35.7 MPa	5180 psi
Tensile Modulus	1.779 - 2.385 GPa	258 - 346 ksi	-	-
Elongation at Break	11 - 20%	11 - 20%	3%	3%
Flexural Strength	59 - 70 MPa	8560 - 10200 psi	-	-
Flexural Modulus	1.882 - 2.385 GPa	273 - 346 ksi	1.56 GPa	226 ksi
Izod Impact, Notched	44 - 49 J/m	0.824 - 0.918 ft-lb/in	-	-
Other Properties	Metric	Imperial	Metric	Imperial
Viscosity	150 - 200 mPa*s	0.00313 - 0.00418 lbf-s/ft2	33 - 57 mPa*s	0.000689 - 0.00119 lbf-s/ft2
Density	1.05 - 1.13 g	0.00232 - 0.00249 lb	-	-
Shrinkage	3.72 - 4.24%	3.72 - 4.24%	2% +/- 1%	2% +/- 1%
Shore Hardness (D)	88	88	82.2	82.2
Glass Transition Temperature	100° C	212° F	-	-
Hot Deformation Temperature	80° C	176° F	-	-

White/Ivory; Grey		Pigment-free
Mechanical Properties	Metric	Imperial	Metric	Imperial
Tensile strength	36  -52 MPa	5220 - 7540 psi	35.7 MPa	5180 psi
Tensile Modulus	1.779 - 2.385 GPa	258 - 346 ksi	-	-
Elongation at Break	11 - 20%	11 - 20%	3%	3%
Flexural Strength	59 - 70 MPa	8560 - 10200 psi	-	-
Flexural Modulus	1.882 - 2.385 GPa	273 - 346 ksi	1.56 GPa	226 ksi
Izod Impact, Notched	44 - 49 J/m	0.824 - 0.918 ft-lb/in	-	-
Other Properties	Metric	Imperial	Metric	Imperial
Viscosity	150 - 200 mPa*s	0.00313 - 0.00418 lbf-s/ft2	33 - 57 mPa*s	0.000689 - 0.00119 lbf-s/ft2
Density	1.05 - 1.13 g	0.00232 - 0.00249 lb	-	-
Shrinkage	3.72 - 4.24%	3.72 - 4.24%	2% +/- 1%	2% +/- 1%
Shore Hardness (D)	88	88	82.2	82.2
Glass Transition Temperature	100° C	212° F	-	-
Hot Deformation Temperature	80° C	176° F	-	-

(ZRESIN-BASIC-WHITE)