Material Overview

KS1208H is a high temp-resistant SLA resin with low viscosity in semi-translucent color. The part can be used at a temperature of around 120℃. For instantaneous temperature, it is resistant to above 200℃. It has good dimensional stability and fine surface details, which is the perfect solution for parts requiring resistance to heat and humidity, and it's also applicable for quick mold with certain materials in small batch production.

Ideal Applications

-    Prototypes need high-temp resistance
-    Quick molds

Advantages

High-temperature resistance

Excellent dimensional stability

High strength and accuracy

Material Parameters

 

  Liquid Properties   Optical Properties
Appearance Semi-translucent Dp 0.115 mm [slope of cure-depth vs. In (E) curve]
Viscosity 340 cps @ 28 °C Ec 13.5 mJ/cm2 [critical exposure]
Density 1.14g/cm3 @ 25 °C Building layer thickness 0.08-0.12mm 0.08-0.12mm
  Mechanical Properties   UV Postcure
TEST ITEMS TEST METHOD NUMERICAL VALUE TEST METHODS NUMERICAL VALUE
Tensile Strength ASTM D 638 65MPa GB/T1040.1-2006 71MPa
Elongation at break ASTM D 638 3-5% GB/T1040.1-2006 3-5%
Bending strength ASTM D 790 110MPa GB/ T9341-2008 115MPa
Flexural modulus ASTM D 790 2720MPa GB/ T9341-2008 2850MPa
Izod notched impact strength ASTM D 256 20J/m GB/T1843-2008 25J/m
Shore hardness ASTM D 2240 87D GB/T2411-2008 87D
Glass transition temperature DMA, tan θ peak 135°C 58 - 70 58 - 70
Thermal expansion coefficient(25-50°C) ASTME831-05 50 μ m/m°C GB/T1036-89 50 μ m/m°C
Thermal expansion coefficient(50-100°C) ASTME831-05 150 μ m/m°C GB/T1036-89 160 μ m/m°C

 

(KS1208H)

SKU KS1208H
Brand Kings
Unit Of Measure each

Be The First To Review This Product!

Help other 3DPrintergear users shop smarter by writing reviews for products you have purchased.

Write a product review